Shedding light on unique conduction mechanisms in a new type of perovskite oxide

Clean energy technologies are the cornerstone of sustainable societies, and solid-oxide fuel cells (SOFCs) and proton ceramic fuel cells (PCFCs) are among the most promising types of electrochemical devices for green power generation. These devices, however, still face challenges that hinder their development and adoption.

Ideally, SOFCs should be operated at low temperatures to prevent unwanted chemical reactions from degrading their constituent materials. Unfortunately, most known oxide-ion conductors, a key component of SOFCs, only exhibit decent ionic conductivity at elevated temperatures. As for PCFCs, not only are they chemically unstable under carbon dioxide atmospheres, but they also require energy-intensive, high-temperature processing steps during manufacture.

Fortunately, there is a type of material that can solve these problems by combining the benefits of both SOFCs and PCFCs: dual-ion conductors. By supporting the diffusion of both protons and oxide ions, dual-ion conductors can realize high total conductivity at lower temperatures and improve the performance of electrochemical devices. Although some perovskite-related dual-ion conducting materials such as Ba₇Nb₄MoO₂₀ have been reported, their conductivities are not high enough for practical applications, and their underlying conducting mechanisms are not well understood.

Against this backdrop, a research team led by Professor Masatomo Yashima from Tokyo Institute of Technology, Japan, decided to investigate the conductivity of materials similar to ₇Nb₄MoO₂₀ but with a higher Mo fraction (that is, Ba₇Nb_4-xMo_1+xO_20+x/2). Their latest study, which was conducted in collaboration with the Australian Nuclear Science and Technology Organisation (ANSTO), the High Energy Accelerator Research Organization (KEK), and Tohoku University, was published in Chemistry of Materials.

After screening various Ba₇Nb_4-xMo_1+xO_20+x/2 compositions, the team found that Ba₇Nb_3.8Mo_1.2O_20.1 had remarkable proton and oxide-ion conductivities. “Ba₇Nb_3.8Mo_1.2O_20.1 exhibited bulk conductivities of 11 mS/cm at 537 ℃ under wet air and 10 mS/cm at 593 ℃ under dry air. Total direct current conductivity at 400 ℃ in wet air of Ba₇Nb_3.8Mo_1.2O_20.1 was 13 times higher than that of Ba₇Nb₄MoO₂₀, and the bulk conductivity in dry air at 306 ℃ is 175 times higher than that of the conventional yttria-stabilized zirconia (YSZ),” highlights Prof. Yashima.

Next, the researchers sought to shed light on the underlying mechanisms behind these high conductivity values. To this end, they conducted ab initio molecular dynamics (AIMD) simulations, neutron diffraction experiments, and neutron scattering length density analyses. These techniques enabled them to study the structure of Ba₇Nb_3.8Mo_1.2O_20.1 in greater detail and determine what makes it special as a dual-ion conductor.

Interestingly, the team found that the high oxide-ion conductivity of Ba₇Nb_3.8Mo_1.2O_20.1 originates from a unique phenomenon. It turns out that adjacent MO₅ monomers in Ba₇Nb_3.8Mo_1.2O_20.1 can form M₂O₉ dimers by sharing an oxygen atom on one of their corners (M = Nb or Mo cation). The breaking and reforming of these dimers gives rise to ultrafast oxide-ion movement in a manner analogous to a long line of people relaying buckets of water (oxide ions) from one person to the next. Furthermore, the AIMD simulations revealed that the observed high proton conduction was due to efficient proton migration in the hexagonal close-packed BaO₃ layers in the material.

Taken together, the results of this study highlight the potential of perovskite-related dual-ion conductors and could serve as guidelines for the rational design of these materials. “The present findings of high conductivities and unique ion migration mechanisms in Ba₇Nb_3.8Mo_1.2O_20.1 will help the development of science and engineering of oxide-ion, proton, and dual-ion conductors,” concludes a hopeful Prof. Yashima.